Types:
08Х18Н10Т, 12Х18Н10Т, 08Х18Н10, 08Х17Т, 08Х18Т1, 12Х17 08Х13
AISI 321, AISI 304(L), AISI 316, AISI 439, AISI 430, AISI 420S
AISI 321, AISI 304(L), AISI 316, AISI 439, AISI 430, AISI 420S
| Standards | Surface type |
|---|---|
| Cold-rolled stainless steel sheet production is based on the following Russian and foreign standards: GOST 5582-75 Corrosion-resistant, heat-resistant GOST 19904-90 Cold-rolled stainless steel sheet. Assortment GOST 4986-76 Cold-rolled corrosion-resistant heat-resistant steel strip TU 14-1-2186-77 Сталь тонколистовая холодноката-ная коррозионностойкая ASTM A480/A480M Standard specification and common requirements for rolled stainless and heat-resistant steel (sheets, plates, strips). |
GOST — М2А, М3А — Cold-rolled, heat-treated, pickled or bright annealed. — М4А — Cold-rolled, heat-treated.ASTM — 2В – Cold-rolled, heat-treated, pickled, rolled-on. — ВА – Cold-rolled, bright annealed. — NA – Cold-rolled, polished.Surface protection РР (paper), РЕ (plastic) One-sided/double-sided By agreement with a client there also can be additional requirements: “For nuclear power plant”, “Aviatechpriemka” (ATP) and ultrasonic examination by continuity class 1-4. |
| Steel type | Gage, mm | Standard size, mm | Surface type | ||||
|---|---|---|---|---|---|---|---|
| 1000х2000 | 1250х2500 | 1500х3000 | 1500х6000 | roll | |||
| 08Х18Н10Т 12Х18Н10Т |
0,5-3,0 | М2А-М4А | |||||
| 08Х18Н10 | 0,5-3,0 | М2А-М4А | |||||
| 08Х17Т 08Х18Т1 |
0,5-3,0 | М2А-М4А | |||||
| 12Х17 08Х13 |
0,5-3,0 | М2А-М4А | |||||
| AISI 321 | 04,-3,0 | 2В, ВА | |||||
| 2,0-6,0 | 2В | ||||||
| AISI 304(L) | 04,-3,0 | 2В, ВА, NA | |||||
| 2,0-6,0 | 2В | ||||||
| AISI 439 | 04,-3,0 | 2В, ВА, NA | |||||
| AISI 430 | 04,-3,0 | 2В, ВА, NA | |||||
| AISI 409 | 04,-3,0 | 2В, ВА, NA | |||||
| Steel type | Chemical composition % | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| GOST | C | Si | Mn | P | S | Cr | Mo | Ni | Ti | Cu |
| ASTM | ||||||||||
| 08X18H10T | <0,08 | <0,80 | ≤2,00 | <0,035 | <0,020 | 17,0-19,0 | 9,0-11,0 | Ti 5xC-0,7 | <0,30 | |
| 12X18H10T | ≤0,12 | <0,80 | ≤2,00 | <0,035 | <0,020 | 17,0-19,0 | 9,0-11,0 | Ti 5xC-0,8 | <0,30 | |
| 321 | ≤0,08 | ≤0,75 | ≤2,00 | 17,0-19,0 | 9,0-12,0 | Ti 5x(C+N) | ||||
| 08X18H10 | <0,08 | <0,80 | ≤2,00 | <0,035 | <0,020 | 17,0-19,0 | 9,0-11,0 | <0,30 | ||
| 304L | ≤0,03 | ≤0,75 | ≤2,00 | 18,0-20,0 | 8,0-12,0 | |||||
| 316L | ≤0,03 | ≤0,75 | ≤2,00 | 16,0-18,0 | 2,0-3,0 | 10,0-14,0 | ||||
| 08X17T | ≤0,08 | <0,80 | <0,80 | <0,035 | <0,020 | 17,0-19,0 | Ti 5x C — 0,8 | <0,30 | ||
| 439 | ≤0,07 | ≤1,00 | ≤1,00 | 17,0-19,0 | Ti(0,20+4(C+N) | |||||
| 08Х18Т1 | ≤0,08 | ≤0,80 | ≤0,07 | <0,035 | <0,020 | 17,0-19,0 | 0,60-1,00 | <0,30 | ||
| 12X17 | <0,12 | <0,80 | <0,80 | <0,035 | <0,020 | 16,0-18,0 | <0,30 | |||
| 430 | ≤0,08 | ≤1,00 | ≤1,00 | 16,0-18,0 | ||||||
| 08X13 | <0,08 | <0,80 | <0,80 | <0,035 | <0,020 | 12,0-14,0 | <0,30 | |||
| 409 | <0,08 | <1,00 | <1,00 | 10,5-12,0 | Ti 6x(C+N) | |||||
| 420S | <0,43-0,48 | <0,75 | <1,00 | 12,0-14,0 | ||||||
| Steel type | Mechanical properties | |||||
|---|---|---|---|---|---|---|
| GOST | Временное сопротивление Н/мм2 (кгс/мм2) |
Tensile Strength, min MPa |
Предел текучести Н/мм2 (кгс/мм2) |
Yield Strength, min MPa |
Относит. удлинение % | Elongation, % |
| ASTM | ||||||
| 08X18H10T | 530(54) | 205(21) | 40 | |||
| 12X18H10T | 530(54) | 205(21) | 40 | |||
| 321 | 515 | 205 | 40 | |||
| 08X18H10 | 510(52) | 185(19) | 45 | |||
| 304L | 515 | 205 | 40 | |||
| 316L | 515 | 205 | 40 | |||
| 08X17T | 460(47) | 30 | ||||
| 439 | 415 | 205 | 22 | |||
| 08Х18Т1 | 460(47) | 30 | ||||
| 12X17 | 490(50) | 20 | ||||
| 430 | 450 | 205 | 22 | |||
| 08X13 | 410(42) | 21 | ||||
| 409 | 450 | 205 | 20 | |||
| 420S | 550 | 380 | 16 | |||