Types:
08Х18Н10Т, 12Х18Н10Т, 08Х18Н10, 10Х17Н13М2Т, 20Х23Н18, 06ХН28МДТ
AISI 321(Н), AISI 304(L), AISI 316(L), AISI 316(Ti), AISI 310S, AISI 904(L)
AISI 321(Н), AISI 304(L), AISI 316(L), AISI 316(Ti), AISI 310S, AISI 904(L)
| Standards | |
|---|---|
| Hot-rolled stainless steel sheet production is based on the following Russian and foreign standards: | |
| GOST 5582-75 Corrosion-resistant, heat-resistant. GOST 19903-74 Hot-rolled stainless steel sheet. Assortment. Protocol 1036 Settled agreement terms of rolled corrosion-resistant, heat-resistant steel thick sheet (OJSC “CMK”)TU 108-903-80 Sheets. Gage 40-160 mm |
ASTM A480/A480M Standard specification and common requirements for rolled stainless and heat-resistant steel (sheets, plates, strips). By agreement with a client there also can be additional requirements: “For nuclear power plant”, “Aviatechpriemka” (ATP) and ultrasonic examination by continuity class 1-4. Service Plasma cutting. Labelling. Delivery. |
Assortment
| Steel type | Gage, mm | Standard size, mm | Surface type | ||||
|---|---|---|---|---|---|---|---|
| 1000х2000 | 1000х4000 | 1250х2500 | 1500х3000 | 1500х6000 | |||
| 08Х18Н10Т 12Х18Н10Т |
4-6 | М2Б-М5Б | |||||
| 6-25 | М2Б-М5Б | ||||||
| 28-100 | 5Г-5Д | ||||||
| 40-160 | М2Б-М4Б, Sandblast method | ||||||
| 08Х18Н10 | 4-6 | М2Б-М5Б | |||||
| 6-25 | М2Б-М5Б | ||||||
| 10Х17Н13М2Т | 4-6 | М2Б-М5Б | |||||
| 6-25 | М2Б-М5Б | ||||||
| 20Х23Н18 | 4-6 | М2Б-М5Б | |||||
| 6-25 | М2Б-М5Б | ||||||
| 06ХН28МДТ | 4-6 | М2Б-М5Б | |||||
| 6-25 | М2Б-М5Б | ||||||
| AISI 321(Н) | 2-6 | 1D(N1) | |||||
| 6-100 | 1D(N1) | ||||||
| AISI 304(L) | 2-6 | 1D(N1) | |||||
| 6-100 | 1D(N1) | ||||||
| AISI 316L AISI 316Ti |
2-6 | 1D(N1) | |||||
| 6-100 | 1D(N1) | ||||||
| AISI 310S | 3-50 | 1D(N1) | |||||
| AISI 904(L) | 2-50 | 1D(N1) | |||||
Chemical composition satisfies GOST 5632-72, ASTM A240
| Steel type | Chemical composition %, for information | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| GOST | C | Si | Mn | P | S | Cr | Mo | Ni | Ti | Cu |
| ASTM | ||||||||||
| 12X18H10T | ≤0,12 | <0,80 | ≤2,00 | <0,035 | <0,020 | 17,0-19,0 | — | 9,0-11,0 | Ti 5xC-0,8 | <0,30 |
| 321 | ≤0,08 | ≤0,75 | ≤2,00 | 17,0-19,0 | — | 9,0-12,0 | Ti 5x(C+N) | — | ||
| 08X18H10T | <0,08 | <0,80 | ≤2,00 | <0,035 | <0,020 | 17,0-19,0 | — | 9,0-11,0 | Ti 5xC-0,7 | <0,30 |
| 321(H) | 0,04-0,10 | ≤0,75 | ≤2,00 | 17,0-19,0 | — | 9,0-11,0 | Ti 4xC(C+N) 07 | — | ||
| 08X18H10 | <0,08 | <0,80 | ≤2,00 | <0,035 | <0,020 | 17,0-19,0 | — | 9,0-11,0 | — | <0,30 |
| 304L | ≤0,03 | ≤0,75 | ≤2,00 | 18,0-20,0 | — | 8,0-12,0 | — | — | ||
| 10Х17Н13М2Т | <0,10 | <0,80 | ≤2,00 | <0,030 | <0,020 | 16,0-18,0 | 2,0-2,5 | 12,0-14,0 | Ti 5x C <0,70 | <0,30 |
| 316L | ≤0,03 | ≤0,75 | ≤2,00 | 16,0-18,0 | 2,0-3,0 | 10,0-14,0 | — | — | ||
| 20Х23Н18 | <0,20 | <1,00 | <2,00 | <0,035 | <0,020 | 22,0-25,0 | — | 19,0-22,0 | — | <0,30 |
| 310S | <0,08 | <1,50 | <2,00 | 22,0-26,0 | 19,0-22,0 | |||||
| 06ХН28МДТ | <0,06 | <0,80 | <0,80 | <0,035 | <0,020 | 22,0-25,0 | 2,50-3,00 | 26,0-29,0 | 0,5-0,9 | 2,5-3,5 |
| 904(L) | <0,02 | <1,00 | <2,00 | 19,0-23,0 | 4,00-5,00 | 23,0-28,0 | 1,0-2,0 | |||
| Steel type | Mechanical properties | |||||
|---|---|---|---|---|---|---|
| GOST | Временное сопротивление Н/мм2(кгс/мм2) | Tensile Strength, min MPa | Предел текучести Н/мм2 (кгс/мм2) | Yield Strength, min MPa | Относит. удлинение % | Elongation, % |
| ASTM | ||||||
| 12X18H10T | 530(54) | 205(21) | 38 | |||
| 321 | 515 | 205 | 40 | |||
| 08X18H10T | 510(52) | 205(21) | 43 | |||
| 321H | 515 | 205 | 40 | |||
| 08X18H10 | 510(52) | 205(21) | 43 | |||
| 304L | 515 | 205 | 40 | |||
| 10Х17Н13М2Т | 510(52) | 196(20) | 40 | |||
| 316L | 515 | 205 | 40 | |||
| 316Ti | 515 | 205 | 40 | |||
| 20Х23Н18 | 540(55) | 265(27) | 35 | |||
| 310S | 515 | 205 | 40 | |||
| 06ХН28МДТ | 540(55) | 215(22) | 35 | |||
| 904(L) | 490 | 220 | 35 | |||